题名: Effect of Oxygen Concentration and Tantalum Addition on the Formation of High Temperature Bismuth Oxide Phase by Mechanochemical Reaction
作者: Hsiu-Na Lin
May-Show Chen
Yu-Hsueh Chang
Pee-Yew Lee
Chung-Kwei Lin
贡献者: 國立臺灣海洋大學:材料工程研究所
关键词: bismuth oxide
phase transformation
high temperature metastable phase
mechanical milling
mechanochemical reaction
日期: 2019-06
上传时间: 2019-06-21T06:12:50Z
出版者: Materials
摘要: Abstract: High-temperature face-centered cubic bismuth oxide phase is a material of great interest
given its unique properties. In the present study, α-Bi2O3 and tantalum powders were used as the
starting powders for the formation of high-temperature bismuth oxide phase via mechanochemical
synthesis by high energy ball milling. (Bi2O3)80(Ta)20 and (Bi2O3)95(Ta)5 in weight concentrations
were milled in either an oxygen-free argon-filled glove box environment or an ambient atmosphere to
investigate the effects of oxygen concentration and tantalum addition. The as-milled powders were
examined using X-ray diffraction, scanning electron microscopy with energy-dispersive spectroscopy,
and differential scanning calorimetry to reveal the structural evolution. The experimental results
showed that for (Bi2O3)95(Ta)5 powder mixtures milled within the glove box, tantalum gradually
reacted with the α-Bi2O3 phase and formed a β-Bi7.8Ta0.2O12.2 phase. For (Bi2O3)80(Ta)20 milled under
the same conditions, Ta and α-Bi2O3 mechanochemically reacted to form δ-Bi3TaO7 and bismuth after
10 min of high energy ball milling, whereas milling (Bi2O3)80(Ta)20 under the ambient atmosphere
with a much higher oxygen concentration accelerated the mechanochemical reaction to less than five
minutes of milling and resulted in the formation of high-temperature δ-Bi3TaO7 phase.
關聯: 12(12)
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/52285
显示于类别:[材料工程研究所] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML35检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈