题名: Enhancement of the energy photoconversion efficiency through crystallographic etching of a c-plane GaN thin film
作者: Antonio M. Basilio
Yu-Kuei Hsu
Wen-Hsun Tu
Cheng-Hsuing Yen
Geng-Ming Hsu
Oliver Chyan
Yieu Chyan
Jih-Shang Hwang
Yit-Tsong Chen
Li-Chyong Chen
Kuei-Hsien Chen
贡献者: 國立臺灣海洋大學:光電科學研究所
日期: 2010-04
上传时间: 2018-12-07T06:47:16Z
出版者: J. Mater. Chemistry
摘要: Abstract: Using a simple and inexpensive crystallographic etching technique on a GaN thin film, the energy photoconversion efficiency was increased by 100%. Prior to etching, the thin film's solar-to-hydrogen conversion efficiency at the applied bias of 0.5 V versus the counter electrode in 1.0 M HCl solution was 0.37%. After etching, the efficiency doubled to 0.75%. After five hours of continuous gas collection, the unetched GaN thin film yielded a stable photocurrent of 0.41 mA cm−2 which produced 0.10 mL of H2 gas. The etched sample, on the other hand, resulted in an improved stable photocurrent of 0.83 mA cm−2 and yielded a greater volume of 0.70 mL of H2 gas, with the presence of H2 confirmed through gas chromatography. Further investigations have shown that the increased hydrogen generation capacity was possibly caused by three factors: one, increase in surface area caused by the etching process; two, decrease in surface donor concentration caused by the etching as probed through Mott-Schottky plots; and three, the appearance of stepped edges and etched facets that show greater photocatalytic activity than the original c-plane when probed through the photodeposition of Ag particles.
關聯: 20(37)
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/51579
显示于类别:[光電科學研究所] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML12检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈