Title: Tool wear and hole quality when single shot drilling of metallic-composite stacks with diamond coated tools.
Authors: C. L. Kuo
S. L. Soo
D. K. Aspinwall
S. Bradley
W. Thomas
R. M’Saoubi
W. Leahy
D. Pearson
Contributors: 國立臺灣海洋大學:商船學系
Keywords: Ti/carbon fibre–reinforced plastic/Al stacks
drilling
diamond coatings
tool life
failure modes
Date: 2014-02
Issue Date: 2018-11-29T03:13:10Z
Publisher: Proceedings of the Institution of Mechanical Engineers, Part B: Journal of Engineering Manufacture
Abstract: Abstract: This article details experimental work performed to evaluate the effects of varying feed rate (0.08 and 0.15 mm/rev) and tool coatings (diamond-like carbon and chemical vapour–deposited diamond) on tool wear modes and hole quality when drilling 30-mm-thick Ti-6Al-4V/carbon fibre–reinforced plastic/Al-7050 stacks in a single-shot operation. At a feed rate of 0.08 mm/rev, the diametrical accuracy of holes produced by both the chemical vapour–deposited diamond and diamond-like carbon–coated drills (6.38 mm diameter) was comparable within a tolerance of ±0.04 mm even after 70 holes. However, in terms of cylindricity, holes machined with chemical vapour–deposited diamond were significantly better than those produced using the diamond-like carbon–coated drills by a factor of ∼2 (65.7 vs 140.6 µm). A similar trend was also observed for hole out of roundness. Burr height at hole entry locations (Ti layer) ranged from ∼0.03 to 0.08 mm for all trials undertaken at the lower feed rate level; however, the diamond-like carbon–coated drills generated exit burrs which were ∼4 times larger than their chemical vapour–deposited diamond-coated counterparts. Subsequent wear analysis showed that diamond-like carbon–coated drills operating at 0.08 mm/rev typically exhibited progressive abrasion, workpiece adhesion and chipping leading to fracture of the tool corner, while fracture due to fatigue was prevalent in tests carried out at the high feed rate level. In contrast, poor adhesion of the chemical vapour–deposited diamond coating to the carbide substrate led to premature flaking, severe chipping and fracture of the drill cutting and chisel edge.
Relation: 228(10) pp.1314-1322
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/51451
Appears in Collections:[商船學系] 期刊論文

Files in This Item:

File Description SizeFormat
index.html0KbHTML10View/Open


All items in NTOUR are protected by copyright, with all rights reserved.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback