Title: The Influence of Microstructures on the Notched Tensile Fracture of Ti–6Al–6V–2Sn Welds at Elevated Temperatures
Authors: Leu Wen Tsay
Chung-Liang Hsu
Chun Chen
Contributors: 國立臺灣海洋大學:光電與材料科技學士學位學程(學系)
Date: 2010-01
Issue Date: 2018-11-20T03:37:58Z
Publisher: ISIJ International
Abstract: Abstract: Notched tensile tests of Ti-6AI-6V-2Sn welds, which were subjected to distinct post-weld heat treatments (PWHTs), were carried out in air at 150, 300 and 450°C. The results were compared with those of mill-annealed base metal (MB) specimens tested at same temperatures. The notched tensile strength (NTS) of the MB specimens decreased significantly with increasing temperature. Moreover, the welds with high hardness showed notch brittleness at room temperature but had a higher NTS than the MB specimen. The presence of grain boundary α layer promoted grain boundary shear, therefore, reduced its notch brittleness at room temperature for the weld with the PWHT at 704°C (the W-704 specimen). A lack of deformation compatibility at the interfaces between the α and β phases caused interfacial separations in the MB specimen as well as void formation in the W-704 specimen, leading to the low NTS of these specimens at elevated temperatures.
Relation: 50(1) pp.128-132
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/51263
Appears in Collections:[光電科學研究所] 期刊論文

Files in This Item:

File Description SizeFormat

All items in NTOUR are protected by copyright, with all rights reserved.


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback