题名: Effect of Zr-content on the oxidation and phase transformation of Zr-base amorphous alloys in air
作者: H.H. Hsieh
W. Kai
R.T. Huang
M.X. Pan
T.G. Niehd
贡献者: 國立臺灣海洋大學:材料工程所
关键词: B. Oxidation
B. Phase transformation
B. Glasses, metallic
日期: 2004-04
上传时间: 2018-10-26T01:25:23Z
出版者: Intermetallics
摘要: Abstract: The oxidation and phase transformation of three Zr-base amorphous alloys, Zr–20Cu–12Ni–10Al–5Ti (Zr53), Zr–30Cu–10Al–5Ni (Zr55), and Zr–15Cu–10Al–10Ni (Zr65), were studied over the temperature range of 300–500 °C in dry air. Oxidation kinetics of these alloys generally followed a parabolic rate law at T>350 °C, but linear kinetics was obeyed at 300–350 °C. It was found that Zr65 was the most oxidation-resistant alloy among the three alloys studied. Scales formed on the alloys during oxidation consisted of mainly tetragonal- and monoclinic-ZrO2 (t- and m-ZrO2), and minor CuO and NiO (only detected in Zr53). The amount of m-ZrO2 formed strongly depends upon the alloy composition, exposure time, and temperature. TEM results showed that a significant amount of nano-grained Zr2Cu polycrystals formed beneath the amorphous oxide-scale in Zr53, indicating phase transformation has taken place. By contrast, Zr55 and Zr65 amorphous substrates transformed into Zr2Cu and ZrAl after oxidation.
關聯: 12(10-11) pp.1089-1096
显示于类别:[材料工程研究所] 期刊論文


档案 描述 大小格式浏览次数



著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈