Title: Sulfide stress corrosion cracking and fatigue crack growth of welded TMCP API 5L X65 pipe-line steel
Authors: L.W.Tsay
Y.C.Chen
S.L.I.Chan
Contributors: 國立臺灣海洋大學:材料工程研究所
Keywords: Slow strain rate tensile test
Fatigue crack growth rates
Hydrogen embrittlement
Quasi-cleavage
Date: 2001-02
Issue Date: 2018-10-23T08:05:39Z
Publisher: International Journal of Fatigue
Abstract: Abstract: Slow strain rate tensile test and fatigue crack growth (FCG) test were performed to evaluate the fracture behavior of API 5L X65 steel weldments after hydrogen-charging. Regardless of the testing environments, tensile fracture of all welds was located at the weld metal (WM), which had the lowest hardness as compared to that of the other parts of the weld. When hydrogen-charged in an H 2S-saturated solution, all specimens suffered a small drop in tensile strength as compared to those tested in air; however, the loss in ductility was more significant. The susceptibility to hydrogen embrittlement of the welds could be reduced significantly by subjecting the welds to 600°C/2 h tempering treatment. With the tempering treatment, the number of surface cracks in the WM after hydrogen-charging decreased and the tensile properties improved. Results of FCG test demonstrated that in a higher stress intensity factor range (Δ K), tempered steel plates with a severely banding structure had the higher fatigue crack growth rates (FCGRs) than those of as-received ones. The WM of an uncharged weld had the lower FCGRs as compared to the parent metal within the same Δ K range. However, the enhancement of crack growth in the WM was very pronounced after hydrogen-charging. SEM fractographs of tensile and fatigue-fractured surfaces revealed a quasi-cleavage fracture in the embrittled region.
Relation: 23(2) pp.103-113
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/50781
Appears in Collections:[Institute of Materials Engineering] Periodical Articles

Files in This Item:

File Description SizeFormat
index.html0KbHTML16View/Open


All items in NTOUR are protected by copyright, with all rights reserved.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback