Title: Fatigue crack propagation in 2.25 Cr–1.0Mo steel weldments in air and hydrogen
Authors: L.W.Tsay
Contributors: 國立臺灣海洋大學:材料工程研究所
Keywords: Fatigue crack growth rates
Weld metal
Heat-affected zone
Fracture feature
Impact toughness
Date: 2001-02
Issue Date: 2018-10-23T08:02:55Z
Publisher: Materials Sci. and Engineering
Abstract: Abstract: Fatigue crack growth (FCG) behaviour of 2.25Cr–1.0Mo steel plate and welds tested in air and gaseous hydrogen was investigated. Microstructural observations indicated that both the weld metal (WM) and heat-affected zone (HAZ) were composed of mainly bainitic microstructure. A ferrite matrix with uniformly dispersed carbides was found in the annealed base metal. The change in microstructures of WM and HAZ between the as-welded and tempered welds was limited. The as-welded WM had the lowest impact toughness among the specimens, however, the impact toughness was improved after postweld heat treatment at 700°C/1 h. Regardless of the testing environments, the as-welded WM exhibited a higher resistance to crack growth than the steel plate as the crack propagated transversely to the welding direction, especially in the low ΔK range. However, higher fatigue crack growth rates in the as-welded HAZ than those of the steel plate were found. As the crack grew along the fine-grained heat-affected zone in the as-welded condition, significant retardation of crack growth as compared with that of the steel plate was obtained when tested in air or gaseous hydrogen. In various regions of the weld, the FCG behaviour of tempered welds was similar to that of the steel plate in air. The results also indicated that the tempered bainitic microstructure present in WM or HAZ was more resistant to unstable crack growth than the annealed steel plate tested in gaseous hydrogen. Environmentally induced acceleration of FCG in various regions of the weld was usually exhibited a change of fracture features.
Relation: 299(1-2) pp.16-26
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/50780
Appears in Collections:[材料工程研究所] 期刊論文

Files in This Item:

File Description SizeFormat

All items in NTOUR are protected by copyright, with all rights reserved.


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback