Title: Embrittlement of laser surface-annealed 17-4 PH stainless steel
Authors: L.W Tsay
T.Y Yang
M.C Young
Contributors: 國立臺灣海洋大學:材料工程研究所
Keywords: Fatigue crack growth
Hydrogen embrittlement
Composite region
Laser annealing treatment
Date: 2001-07
Issue Date: 2018-10-23T07:59:21Z
Publisher: Mats. Sci. Engineering A
Abstract: Abstract: Stress corrosion cracking and fatigue crack growth behavior were determined in 17-4 PH stainless steel under various metallurgical conditions, including the H900 (482°C/1 h), H1025 (552°C/4 h) aging and laser surface annealing treatments. Peak-aged (H900) specimens locally irradiated by laser beam consisted of a portion of composite region (CR), in which comprised of soft laser-annealed (LA) zones on the outer surfaces and the hard base metal in between. Slow extension rate tensile tests were performed at room temperature in a saturated H2S solution to evaluate the hydrogen embrittlement susceptibility of various specimens. H900 specimens show an obvious improvement in impact toughness after irradiating by laser. Regardless of testing environments, H900 specimens exhibited better tensile properties than the other specimens. Experimental results also indicated that H900 specimens had the highest fatigue crack growth rates among the specimens, particularly at low stress intensity factor range. The retardation of crack growth in the region ahead of the CR in the LA specimens was rather pronounced. For compact tension specimens tested in gaseous hydrogen, enhanced crack growth was correlated with quasi-cleavage fracture in contrast to transgranular fatigue fracture in air.
Relation: 311(1-2) pp.64-73
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/50779
Appears in Collections:[材料工程研究所] 期刊論文

Files in This Item:

File Description SizeFormat

All items in NTOUR are protected by copyright, with all rights reserved.


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback