题名: Influence of gaseous hydrogen on the notched tensile strength of D6ac steel
作者: T.L. Chang
L.W. Tsay
C. Chen
贡献者: 國立臺灣海洋大學:材料工程研究所
关键词: Notched tensile strength
D6ac steel
Gaseous hydrogen embrittlement
日期: 2001-11
上传时间: 2018-10-23T07:50:08Z
出版者: Mats. Sci. Engineering A
摘要: Abstract: Slow displacement-rate tensile tests were performed on D6ac tempered specimens to investigate the influence of gaseous hydrogen pressure on the notched tensile strength (NTS) and the associated fracture characteristics. The susceptibility to hydrogen embrittlement of specimens at a given pressure was determined by the NTS loss, which tended to decrease as the tempering temperature increased. The NTS loss for T-300 (300°C tempered) and T-450 (450°C tempered) specimens increased with rising hydrogen pressure up to 5×105 Pa and then remained nearly the same up to the pressure of 2×106 Pa, while no deteriorated NTS in hydrogen has been found for T-600 (600°C tempered) specimens. The extent of intergranular fracture and/or the region of flat fracture on tensile fractured surfaces were consistent with the correlation of hydrogen pressure and NTS loss. The smaller the intergranular and/or flat fracture regions, the greater the resistance to hydrogen embrittlement of the specimen would be expected. Besides the effect of notch tip blunting, the excellent performance of T-600 specimens in hydrogen could be attributed partly to the presence of less continuous carbides at prior austenite grain boundaries. In contrast, T-300 specimens with grain boundary carbides in a more continuous manner were highly susceptible to hydrogen embrittlement.
關聯: 316(1-2) pp.153-160
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/50777
显示于类别:[材料工程研究所] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML15检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈