Title: The effect of residual thermal stresses on the fatigue crack growth of laser-annealed 304 stainless steels
Authors: L.W.Tsay
M.C.Young
F.Y.Chou
R.K.Shiue
Contributors: 國立臺灣海洋大學:材料工程研究所
Keywords: Laser annealing
Fatigue crack growth
Residual thermal stresses
AISI 304 stainless steels
Date: 2004-12
Issue Date: 2018-10-22T08:21:04Z
Publisher: Mat. Chem. Phy. Sci.
Abstract: Abstract: The fatigue crack growth behavior of AISI 304 stainless steels annealed by a CO2 laser was investigated in the study. For the laser-annealed specimen prior to introducing a notch, the residual tensile stress was obtained around the center of the laser-annealed zone (LAZ), and the residual stress field changed gradually from tensile into compressive stress with increasing the distance away from the centerline of LAZ. Based on the experimental result, the laser-annealed specimen tested under low ΔK had a higher resistance to fatigue crack growth in the region preceding the LAZ after introducing a notch perpendicular to the LAZ. In contrast, the retardation of fatigue crack growth disappeared for the laser-annealed specimen stress-relieved at 850 °C for one hour. The presence of residual compressive stress field ahead of the crack tip resulted in the decreased fatigue crack growth rate (FCGR). Moreover, residual compressive stresses enhanced the effect of crack closure, and led to the formation of rubbed marks on the fatigue-fractured surface. As the fatigue crack propagated further into the LAZ, the residual tensile stress field ahead of crack tip did not accelerate the crack growth. The results indicated that tensile stress field ahead of the crack tip had little effect on the FCGR of the ductile 304 stainless steel.
Relation: 88(2-3) pp.348-352
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/50749
Appears in Collections:[材料工程研究所] 期刊論文

Files in This Item:

File Description SizeFormat
index.html0KbHTML23View/Open


All items in NTOUR are protected by copyright, with all rights reserved.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback