题名: The Evolution of Cast Microstructures on the HAZ Liquation Cracking of Mar-M004 Weld
作者: Yi-Hsin Cheng
Jyun-Ting Chen
Ren-Kae Shiue
Leu-Wen Tsay
贡献者: 國立臺灣海洋大學:材料工程研究所
关键词: liquation crack
heat-affected zone
Mar-M004 superalloy
repair welding
日期: 2018-04
上传时间: 2018-10-22T07:57:32Z
出版者: Metals
摘要: Abstract: The causes of liquation cracking in the heat-affected zone (HAZ) of a cast Mar-M004 superalloy weld were investigated. X-ray diffraction (XRD), electron probe microanalyzer (EPMA), and electron backscatter diffraction (EBSD) were applied to identify the final microconstituents at the solidification boundaries of the cast alloy. Fine borides and lamellar eutectics were present in front of some γ-γ′ colonies, which were expected to be liquefied prematurely during welding. The metal carbide (MC) enriched in Nb, Hf; M3B2 and M5B3 borides enriched in Cr and Mo; and lamellar Ni-Hf intermetallics were mainly responsible for the induced liquation cracking of the Mar-M004 weld, especially the MC carbides. Scanning electron microscope (SEM) fractographs showed that the fracture features of those liquation cracks were associated with the interdendritic constituents in the cast superalloy.
關聯: 8(1)
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/50739
显示于类别:[材料工程研究所] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML35检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈