题名: Structure and luminescence of core-shell phosphor aluminate-boron oxide
作者: Chen-Yu Wu
Chien-Ming Lei
Toshiaki Takei
Rudder Wu
Shing-Hoa Wang
Chau-Chang Chou
Horng-Yi Chang
贡献者: 國立臺灣海洋大學:輪機工程學系
关键词: Luminescence
Phosphor
Hydrothermal
Afterglow
日期: 2018-04
上传时间: 2018-08-28T08:10:56Z
出版者: Journal of Alloys and Compounds
摘要: Abstract: Long-afterglow phosphor SrAl2O4: 0.01Eu2+, 0.01Dy3+ (SAO) requires a high sintering temperature of 1400 °C even when boric acid is added as flux via a solid-state reaction. The aluminum source NaAlO2 behaved as a good mineralizer in the designed hydrothermal process to achieve a large surface-to-thickness ratio of SAO. The flower-like shape of hydrothermally prepared hSAO without B2O3 after annealing at 1100 °C/4 h transformed into a rod-like plate phosphor with nano-thickness. Such a small rod-like plate exhibited higher photoluminescence (PL) intensity than large-grained B2O3-added bSAO prepared via a solid-state reaction. The annealed hSAOs inherited the morphology of the as-hydrothermally prepared aluminates. A nano-thick sheet of annealed aSAO containing B2O3 further enhanced the PL significantly and indicated a blue shift independent of the grain size. Furthermore, the nano-thick sheet of phosphors exhibited the same afterglow as the conventional tens-of-micrometers-sized phosphors. Fourier-transform infrared spectroscopy and X-ray diffraction results showed that the BO4 bond may substitute AlO4 in the structure and the BO3 bond is in a flux outside the annealed aSAO and bSAO grains. The molten flux formed a thin layer on the surface of the SAO particles to be a core-shell of the SAO-B2O3 structure, behaving as a diffusion-assistant medium and environmental protection layer against acid and humidity.
關聯: 743 pp.506-513
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/49931
显示于类别:[輪機工程學系] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML61检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈