题名: Chemical inertness of Cr–W–N coatings in glass molding
作者: Yung-I Chen
Yu-Ru Cheng
Li-Chun Chang
Jyh-Wei Lee
贡献者: 國立臺灣海洋大學:光電與材料科技學系
关键词: Annealing
Glass molding
Mechanical properties
Oxidation
Cr–W–N
日期: 2015-10
上传时间: 2018-08-16
出版者: Thin Solid Films
摘要: Abstract: Cr–W–N coatings with a Cr interlayer were prepared using reactive direct-current magnetron cosputtering on Si and cemented carbide substrates. To investigate the chemical inertness of Cr–W–N coatings against commercial moldable SiO2–B2O3–BaO-based glass in glass molding, thermal cycle annealing at 270 °C and 600 °C was performed in a quartz tube furnace in a 15-ppm O2–N2 atmosphere. Variations in the crystalline structure, mechanical properties, and surface roughness after various annealing durations were investigated. The results indicated that Cr37W31N32 and Cr24W46N30 coatings maintained a face-centered cubic phase and exhibited superior mechanical properties and low surface roughness after up to 1000 thermal cycles; these properties were attributed to the formation of amorphous oxide scales. By contrast, Cr8W69N23 and Cr4W82N14 coatings with a nanocrystalline W phase in the as-deposited state formed WO3 oxide scales after annealing, which negatively affected their mechanical properties and raised surface roughness values.
關聯: 593 pp.102-109
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/48191
显示于类别:[光電科學研究所] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML12检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈