Title: Notched tensile fracture of Ti6Al4V laser welds at elevated temperatures
Authors: M. Y. Lu
L. W. Tsay
C. Chen
Contributors: 國立臺灣海洋大學:光電與材料科技學系
Keywords: notched tensile test
laser welding
post-weld heat treatment
Date: 2012-06
Issue Date: 2018-08-15T03:01:10Z
Publisher: Materials Transactions
Abstract: Abstract: Notched tensile tests of Ti–6Al–4V laser welds that were subjected to post-weld heat treatments (PWHTs) at 482 and 704°C were carried out in air at temperatures from 25 to 450°C. The experimental results were also compared with those of the mill-annealed base metal (MB) specimens tested at similar temperatures. Generally, the notched tensile strength (NTS) of the specimens was sensitive to the test temperature. The NTS of laser welds was lower than that of the MB specimen at room temperature, but the trend reversed at 450°C. The presence of thick grain boundary α layers, which promoted intergranular fracture at elevated temperatures, could account for the lowered NTS of the weld after PWHT at 704°C.
Relation: 53(6) pp.1042-1047
Appears in Collections:[Institute of Optoelectronic Sciences] Periodical Articles

Files in This Item:

File Description SizeFormat

All items in NTOUR are protected by copyright, with all rights reserved.


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback