题名: The effect of phase transformation in the plastic zone on the hydrogen-assisted fatigue crack growth of 301 stainless steel
作者: T.C. Chen
S.T. Chen
W. Kai
L.W. Tsay
贡献者: 國立臺灣海洋大學:光電與材料科技學系
关键词: Stainless steel
Fatigue crack growth rate
Hydrogen embrittlement
日期: 2016-02
上传时间: 2018-08-14T08:12:20Z
出版者: Materials Characterization
摘要: Abstract: The effects of rolling and stress ratio (R) on the fatigue crack growth rates (FCGRs) of AISI 301 stainless steel (SS) in gaseous hydrogen were investigated. Accelerated fatigue crack growth occurred for the solution-annealed (SA) and cold rolled (CR) specimens tested in gaseous hydrogen, and especially for the CR specimen at high R. Moreover, a sufficiently high ΔK and/or Kmax were required to activate hydrogen-assisted fatigue crack growth of the 301 SS. Fatigue crack growth within a narrow α′ martensite layer was responsible for the rapid FCGRs of the specimens in hydrogen. The plastic zone size, identified by hardness distributions, was much larger than the region that underwent phase transformation.
關聯: 112 pp.134-141
显示于类别:[光電科學研究所] 期刊論文


档案 描述 大小格式浏览次数



著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈