題名: Angular dispersion of the easy axis in a magnetically soft film as determined by vibrating sample magnetometer.
作者: W. L. Chen
S. U. Jen
貢獻者: 國立臺灣海洋大學:光電科學研究所
日期: 2000-06
上傳時間: 2018-07-05T01:03:56Z
出版者: J. Appl. Phys.
摘要: Abstract: In this paper, we briefly described how to use the vector or biaxial vibrating sample magnetometer (VSM) to determine the angular dispersion of easy axis in a magnetically soft film. For each angle of rotation φ of the external field H, a pair of the Mx-hysteresis and My-hysteresis loops could be obtained. Then, we changed the φ setting from negative to positive, with φ=0° indicating the exact direction of the hard axis of the film. Note, the easy axis has been induced by a deposition field h during fabrication of the film. From the characteristics of the Mx-hysteresis and My-hysteresis loops, the condition |φ|<φc≅1° defines the “in-center zone,” and the condition |φ|>φc defines the “off-center zone.” The types of switching modes for the in-center and off-center zones, respectively, are different. Only the hysteresis behaviors in the latter zone are understood well for detailed explanations. Then, the normalized change ΔMy/MS due to the wall motions at the switching field |H|=HSW can be used to indicate the angular dispersion Δθ in the film. Co70Fe10Ni20 films were made with various deposition conditions in order to cause different degrees of dispersion in them. The result shows that it is possible to study the angular dispersion in a magnetically soft film via the vectorial VSM measurements.
關聯: 87(12)
顯示於類別:[光電科學研究所] 期刊論文


檔案 描述 大小格式瀏覽次數



著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋