題名: Magnetic properties of Fe-rich Fe–V alloy films
作者: 任盛源
貢獻者: 國立臺灣海洋大學:光電科學研究所
日期: 2009-07
上傳時間: 2018-07-04T07:15:07Z
出版者: J. Appl. Phys.
摘要: ABSTRACT: Polycrystalline Fe100−xVx with x=0 to 14 at.% V films on a glass substrate were made by the dc magnetron sputtering method. The deposition temperature was 250 °C. The magnetic properties, i.e., saturation magnetization 4πMs, bulk-pinning field for a domain wall Hcw, coercive force Hc, initial permeability μi, maximum permeability μm, saturation magnetostriction λs, and electrical property, such as the electrical resistivity ρ of the Fe–V films, were measured. We find that 4πMs is a decreasing function of x, Hc, and/or Hcw has a minimum at x≈x0=8 at. % V, μi, μm, and/or μc has a maximum at x=x0, λs≈0 at x=x0, and ρ is an increasing function of x. These new magnetic results are consistent with earlier magnetostriction measurements [Jen and Chen, J. Magn. Magn. Mater. 204, 165 (1999)] and theoretical calculations [Ostanin, Staunton, and Razee, Phys. Rev. B 69, 064425 (2004)]. Moreover, all the magnetic features in the x dependence of Hc, Hcw, μi, μm, μc, and λs, respectively, can be explained within the framework of the bulk-pinning (or surface-pinning) and the end-pinning (or nucleation) models. Briefly, the pinning model analysis of the magnetic hysteresis data confirms the inference that near zero λs implies maximal permeabilities and smallest Hc and Hcw. Among all the Fe–V films, the Fe92V8 film has the optimal magnetic and electrical properties for application.
關聯: 106(1)
顯示於類別:[光電科學研究所] 期刊論文


檔案 描述 大小格式瀏覽次數



著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋