题名: Deep and Alignment Free Patterned Etching of GaN Surface Using an Atomic Force Microscope
作者: Hwang JS;Chen DC;Chen LW;Hu ZS;You ZY;Wu CC;Lin TY;Tsai TR;Chattopadhyay S.
贡献者: 國立臺灣海洋大學:光電科學研究所
日期: 2011
上传时间: 2017-02-13T02:53:40Z
出版者: Journal of Nanosci Nanotechnology
摘要: Abstract: Successful deep and alignment-free patterned etching on GaN using atomic force microscope (AFM) local oxidation followed by in-situ chemical etching is demonstrated. Oxide ridges are grown on GaN on an AFM by applying positive sample bias at 80% humidity, with the oxidation reaction expedited by UV light. The oxide ridges are then etched by HCl solution, leaving troughs in the GaN surface. A dripping strategy for the in-situ chemical etching is recommended that allows deep, alignment-free multiple AFM oxidation/etching works on the GaN surface without any need of substrate removal from the AFM platform. Repeated etching followed by AFM oxidation on a spot on a GaN surface resulting in a hole as deep as 800 nm was also demonstrated. Further, a preliminary evaluation of the porosity of the AFM-grown oxide indicates that the oxide ridges grown on GaN at an AFM cantilever moving speed of 300 nm/s are porous in structure, with an estimated porosity of 86%, which porosity could be reduced if longer resident time of the AFM cantilever on the target oxidation region was used.
显示于类别:[光電科學研究所] 期刊論文


档案 描述 大小格式浏览次数



著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈