题名: Rotation-field annealing effect on magnetoimpedance of Co-based amorphous ribbons
作者: S.U. Jen
H.P. Chiang
H.D. Liu
C.C. Chang
贡献者: 國立臺灣海洋大學:光電科學研究所
关键词: Co-based amorphous ribbon
日期: 2010
上传时间: 2017-02-10T02:44:20Z
出版者: Journal of Alloys and Compounds
摘要: Abstract
A new annealing method, called the RFA method, is introduced to improve the magnetoimpedance (MI) effect in Co-based amorphous ribbons; e.g. VAC6025. This method includes applying a sufficiently large rotating field hR, with a frequency F from 1 to 100 Hz, when the ribbon sample has been at the annealing temperature TA (from 160 to 280 °C) for 1 h, and then is field-cooled to room temperature. The best achievements are that: [I] after the F = 1 or 50 Hz and TA = 200 °C RFA treatment, the maximum MI ratio (ΔZ/Z)m = 72% and the maximum operating frequency fm = 0.6 MHz; [II] after the F = 50 Hz and TA = 160 °C RFA treatment, the maximum field sensitivity Sm = 4.5%/Oe and the highest figure of merit FOM = 1.8% MHz/Oe; [III] since both of the optimal TAs above are much lower than the crystallization temperature (TX = 500 °C), the samples remain ductile after RFA. In conclusion, we believe that the RFA treatment can greatly improve the MI performance of the VAC6025 ribbons, since hR, operating at TA and/or below, can effectively randomize the magnetic anisotropy, and thereby reduce the effective (or average) anisotropy energy 〈K〉. This is equivalent to stating that the RFA method is effective in enhancing the permeability or the ΔZ/Z ratio of any amorphous ribbon sample, including VAC6025.
關聯: 508(2)
显示于类别:[光電科學研究所] 期刊論文


档案 描述 大小格式浏览次数



著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈