Title: Surface Modification of Ultra-High Molecular Weight Polyethylene with Crosslinked Hyaluronic Acid and its Antiwear Performance
Authors: Chau-Chang Chou;Yu-Hsiang Hao;Fu-Yin Hsu
Contributors: 國立台灣海洋大學:生命科學系
Date: 2015
Issue Date: 2016-05-09T01:59:02Z
Publisher: Key Engineering Materials
Abstract: ABSTRACT:
The surface of high-pressure crystallized ultra-high molecular weight polyethylene (UHMWPE) was modified for application as an artificial cartilage material. A UHMWPE surface pretreated by a series of processes, including treatment with O2-plasma and ethylenediamine solution, was coated with hyaluronic acid (HA). After that, adipic acid dihydrazide (AAD) was added to partially crosslink the HA coating in order to enhance its durability. The modified samples were verified by water contact angle measurement and Fourier transform infrared spectrometry. Both HA layers, original and crosslinked, were also quantitatively evaluated by carbohydrate chemistry assay according to the absorbance of the incident light. The tribological performance of the samples was evaluated by a pin-on-disk test rig lubricated by normal saline under an average pressure of 18 MPa and at a sliding speed of 0.03 m/s for 45 h. The wear resistance of the HA-coated UHMWPE specimens promoted by the crosslink process was superior to that of the original HA-coated sample, and that resistance was maintained after immersion in saline solution for one month.

Surface Modification of Ultra-High Molecular Weight Polyethylene with Crosslinked Hyaluronic Acid and its Antiwear Performance (PDF Download Available). Available from: https://www.researchgate.net/publication/272498255_Surface_Modification_of_Ultra-High_Molecular_Weight_Polyethylene_with_Crossc_Acid_and_its_Antiwear_Performancelinked_Hyaluroni
Relation: 642(94)
URI: http://ntour.ntou.edu.tw:8080/ir/handle/987654321/37771
Appears in Collections:[生命科學系] 期刊論文

Files in This Item:

File Description SizeFormat

All items in NTOUR are protected by copyright, with all rights reserved.


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback