题名: Preparation and properties of lead-zirconate-titanate ferroelectric thin films using radio frequency planar magnetron sputtering
作者: C. C. Chang;C. S. Tang
贡献者: NTOU:Department of Electrical Engineering
國立臺灣海洋大學:電機工程學系
日期: 2000
上传时间: 2011-10-21T02:40:29Z
出版者: Journal of Applied Physics
摘要: Abstract:Lead-zirconate-titanate [Pb(Zr52Ti48)O3,PZT] thin films, 0.5 μm thick, were deposited onto Pt/Si substrate at room temperature using the radio frequency planar magnetron sputtering technique. A perovskite structure in the PZT thin film was obtained after the annealing processes. The annealing temperature varied from 650 to 750 °C in this experiment to find the optimized annealing temperature. Using x-ray diffraction analysis, the lowest full width of the half maximum (110) plane was 0.23° for the sample at 650 °C annealing temperature. The values of the remanent polarization Pr and coercive field Ec of the PZT thin film were 100 nC cm−2 and 0.6 kV cm−1, respectively, at 60 Hz. The measured pyroelectric coefficient in 0.5 μm thin films was 3.12×10−4 C/m2 K at 50 °C. Their dielectric constant and loss tangent were 494 and 0.072, respectively, at 1 kHz. The surface structure of the PZT thin film was examined using scanning electron microscopy and the grain size was in the range of 0.08–0.14 μm.
關聯: 87(8), pp.3931-3936
URI: http://ntour.ntou.edu.tw/handle/987654321/28787
显示于类别:[電機工程學系] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML290检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈