题名: Growth and characterization of well aligned densely packed IrO2 nanocrystals on sapphire via reactive sputtering
作者: Alexandru Korotcov;Ying-Sheng Huang;Dah-Shyang Tsai;Kwong-Kau Tiong
贡献者: NTOU:Department of Electrical Engineering
國立臺灣海洋大學:電機工程學系
日期: 2006
上传时间: 2011-10-21T02:37:47Z
出版者: Journal of Physics: Condensed Matter
摘要: Abstract:Well aligned densely packed IrO2 nanocrystals (NCs) have been grown on sapphire (SA) substrates with different orientations by reactive magnetron sputtering using an Ir metal target. The surface morphology, structural and spectroscopic properties of the as-deposited NCs were characterized using field-emission scanning electron microscopy (FESEM), x-ray diffraction (XRD), x-ray photoelectron spectroscopy (XPS) and micro-Raman spectroscopy. FESEM micrographs reveal that NCs with parallel in-plane alignment were gown on SA(001), vertically aligned NCs were grown on SA(100), while the NCs on SA(012) and SA(110) contained, respectively, single- and double-aligned directions with a tilt angle of ~35° from the normal to the substrates. The XRD results indicate that the NCs are (100), (001), and (101) oriented on SA(001), SA(001), and SA(012)/SA(110) substrates, respectively. A strong substrate effect on the alignment of the IrO2 NCs growth has been demonstrated and the probable mechanism for the formation of these NCs has been discussed. XPS analyses show the coexistence of higher oxidation states of iridium in the as-grown IrO2 NCs. The Raman spectra show the red-shift and asymmetric peak broadening with a low frequency tail of the IrO2 signatures with respect to that of the bulk counterpart, which are attributed to both the size and residual stress effects.
關聯: 18(4), pp.1121-1136
URI: http://ntour.ntou.edu.tw/handle/987654321/28494
显示于类别:[電機工程學系] 期刊論文

文件中的档案:

档案 描述 大小格式浏览次数
index.html0KbHTML373检视/开启


在NTOUR中所有的数据项都受到原著作权保护.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回馈