題名: Structural and nanoscale electrical properties of bismuth ferrite thin films annealed in forming gas
作者: Yuan-Chang Lian
貢獻者: NTOU:Institute of Materials Engineering
國立臺灣海洋大學:材料工程研究所
關鍵詞: Thin Films;Topography;Forming gas annealing;Bismuth ferrite;Nanoscale electrical properties;Microstructures
日期: 2010-08
上傳時間: 2011-10-20T08:07:41Z
出版者: Abstract proceedings of the 18th international vacuum congress (IVC-18)
摘要: The 60 nm-thick BiFeO3 (BFO) thin films with (h00) orientation were successfully grown on the LaNiO3(LNO)-buffered Pt/Ti/SiO2/Si(100) substrates. The effect of forming gas (7%H2+93%Ar) annealing (FGA) temperature (300-500) on the physical properties of the BFO thin films is investigated in this study. The x-ray diffraction results show that the higher FGA temperature results in a larger degree of deterioration of crystal quality of the BFO thin films. This change can be attributed to a loss of oxygen from the BFO thin films and the incorporation of hydrogen atoms into the lattice of the BFO thin films during FGA at a high temperature. FGA incurs an increase in surface roughness of the BFO thin films. The current maps obtained by the measurements of conductive atomic force microscope demonstrate that the leakage behaviors of BFO thin films without and with FGA at various temperatures under the breakdown electric field are different. The leakage currents are detected mostly in areas around large crystallites for BFO thin films without or with FGA at 300. In contrast, large crystallites in the BFO thin films with FGA at 400-500 are electrically leaky and the detected currents are high compared to those of BFO thin films without and with FGA at 300.
URI: http://ntour.ntou.edu.tw/handle/987654321/23739
顯示於類別:[材料工程研究所] 演講及研討會

文件中的檔案:

沒有與此文件相關的檔案.



在NTOUR中所有的資料項目都受到原著作權保護.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - 回饋