Title: Microstructure and Notch Properties of Heat-Treated Ti-4.5Al-3V-2Mo-2Fe Laser Welds
Authors: Wei-Chih Chung;Leu-Wen Tsay;Chun Chen
Contributors: NTOU:Institute of Materials Engineering
國立臺灣海洋大學:材料工程研究所
Keywords: Ti-4.5Al-3V-2Mo-2Fe;microstructure;notch properties;heat treatment;laser welding;impact toughness;notched tensile strength
Date: 2009
Issue Date: 2011-10-20T08:07:28Z
Publisher: Materials Transactions(The Japan Institute of Metals)
Abstract: Abstract: The microstructure and transformation behavior of Ti-4.5Al-3V-2Mo-2Fe alloy and its laser welds after various heat treatments were investigated. Notch properties, such as impact toughness and notched tensile strength, were also measured on the welds to choose an appropriate post-weld heat treatment (PWHT) of the alloy. The temperature regimes in which β transformed into α', α'' or retained as β after quenching were identified and discussed. The results indicated that α'' could be obtained primarily by rapid quenching from 880∼840°C solution temperatures and was identified as a base-centered orthorhombic (centered on the C face) with the lattice parameters of a=0.305 nm, b=0.489 nm, and c=0.457 nm. The as-welded specimen exhibited fine acicular α in the β matrix with hardness considerably higher than the mill-annealed base metal. For a PWHT temperature lower than 800°C, the change in microstructure and hardness of the welds depended mainly on the temperature, not on the cooling rate. If the PWHT temperature was higher than 800°C, both the temperature and the cooling rate were important in altering microstructure and hardness of the welds. The welds after a 704°C/4 h treatment could prevent notch brittleness, reduce hardness variation in different regions of the weld, and obtain notch properties similar to the mill-annealed base metal.
Relation: 50(03), pp.544-550
URI: http://ntour.ntou.edu.tw/handle/987654321/23718
Appears in Collections:[Institute of Materials Engineering] Periodical Articles

Files in This Item:

File Description SizeFormat
index.html0KbHTML262View/Open


All items in NTOUR are protected by copyright, with all rights reserved.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback