Title: Growth-Temperature-Dependent Electrical Properties of Mn Doping Ba0.5Sr0.5TiO3 Thin Films on La0.72Ca0.28MnO3 Electrodes
Authors: Yuan-Chang Liang;J. P. Chu
Contributors: NTOU:Institute of Materials Engineering
Keywords: characterization;oxides;perovskites;doping
Date: 2007
Issue Date: 2011-10-20T08:07:19Z
Publisher: Japanese Journal of Applied Physics
Abstract: Abstract:Ba0.5Sr0.5TiO3 (BST) thin films doped with 3 mol % Mn were fabricated on La0.72Ca0.28MnO3-coated SrTiO3(001) substrates. The effects of growth temperature and Mn doping on the lattice and electrical properties of the BST films were studied. Mn-doped BST films have rougher surfaces and larger grains than undoped BST films. Adding Mn dopants to BST films improves their dielectric constant, tunability, and leakage-current characteristics. Additionally, the degree of improvement of the electrical characteristics of the Mn-doped BST film depends strongly on the growth temperature. The higher growth temperature of the Mn-doped BST film is associated with a greater improvement in the dielectric constant and a more favorable figure of merit than in the undoped case. The tunability of the Mn-doped BST film that was deposited at 750 °C was enhanced from 41 to 60%; the figure of merit increased from 13 to 53, and the leakage current density was approximately one order of magnitude lower than that of the undoped film at an applied electric field of 300 kV/cm. The results demonstrate that Mn-doped BST films with appropriately controlled growth temperatures have potential for use in tunable devices.
Relation: 47, pp.257-261
Appears in Collections:[Institute of Materials Engineering] Periodical Articles

Files in This Item:

File Description SizeFormat

All items in NTOUR are protected by copyright, with all rights reserved.


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback