Title: Effect of austenite instability on the hydrogen-enhanced crack growth of austenitic stainless steels
Authors: L.W. Tsay;S.C. Yu;R.-T. Huang
Contributors: NTOU:Institute of Materials Engineering
國立臺灣海洋大學:材料工程研究所
Keywords: A. Austenitic stainless steel;C. Hydrogen embrittlement;C. Fatigue crack growth
Date: 2007-07
Issue Date: 2011-10-20T08:07:00Z
Publisher: Corrosion Science
Abstract: Abstract:Fatigue crack growth tests were performed to assess the fatigue behavior of AISI 316L and 254 SMO stainless steels (SSs) in air and gaseous hydrogen. 254 SMO SS generally exhibited a greater resistance to fatigue crack growth than 316L. Sensitization treatment had only a marginal effect on the fatigue crack growth behavior of both alloys in air. Moreover, 316L SS exhibited significant hydrogen-enhanced crack growth but 254 SMO, even sensitized 254 SMO specimens, did not. A thin layer of strain-induced martensite was formed on the fatigue-fractured surface of the 316L SS, and its content increased when raising the stress ratio. The thin martensite layer was responsible for the hydrogen-enhanced fatigue crack growth of the 316L SS. By contrast, the extremely stable austenite was responsible for the low susceptibility of 254 SMO SS to hydrogen-accelerated crack growth. The trapping of hydrogen at the grain boundaries and the transformed martensite in the sensitized 316L specimens led to increased fatigue crack growth rates and intergranular fracture of the material.
Relation: 49(7), pp.2973-2984
URI: http://ntour.ntou.edu.tw/handle/987654321/23654
Appears in Collections:[Institute of Materials Engineering] Periodical Articles

Files in This Item:

There are no files associated with this item.



All items in NTOUR are protected by copyright, with all rights reserved.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback