Title: Formation and Characterization of Mechanically Alloyed Ti-Cu-Ni-Sn Bulk Metallic Glass Composites
Authors: I-Kuan Jeng;Chung-Kwei Lin;Pee-Yew Lee
Contributors: NTOU:Institute of Materials Engineering
國立臺灣海洋大學:材料工程研究所
Keywords: A. Composites;A. Glasses, metallic;B. Mechanical properties at ambient temperature;C. Mechanical alloying and milling
Date: 2006-08
Issue Date: 2011-10-20T08:06:33Z
Publisher: Intermetallics
Abstract: Abstract:In the present study, amorphous Ti50Cu28Ni15Sn7 and its composite powders reinforced with 4, 8, and 12 vol.% of W additions were prepared by mechanical alloying. After 5 h of milling, amorphous powders with homogeneously dispersed W nanoparticles were synthesized. The as-milled Ti50Cu28Ni15Sn7 and composite powders were then consolidated by vacuum hot pressing into disc compacts with a diameter and thickness of 4 and 10 mm, respectively.
The structure of the as-milled powders and consolidated compacts was characterized by X-ray diffraction (XRD), scanning electron microscopy, and transmission electron microscopy. While the thermal stability was examined by differential scanning calorimeter (DSC). In addition, the mechanical property of the consolidated BMGs was evaluated by Vickers microhardness tests. The experimental results showed that W nanoparticles ranged from 20 to 200 nm were embedded within the amorphous matrix. The presence of W nanoparticles did not dramatically change the glass formation ability of amorphous Ti50Cu28Ni15Sn7 powders. While the thermal stability of amorphous powders differed from those of its composites. A significant hardness increase with W additions was noticed for consolidated composite compacts.
Relation: 14(8-9), pp.957-961
URI: http://ntour.ntou.edu.tw/handle/987654321/23538
Appears in Collections:[材料工程研究所] 期刊論文

Files in This Item:

There are no files associated with this item.



All items in NTOUR are protected by copyright, with all rights reserved.

 


著作權政策宣告: 本網站之內容為國立臺灣海洋大學所收錄之機構典藏,無償提供學術研究與公眾教育等公益性使用,請合理使用本網站之內容,以尊重著作權人之權益。
網站維護: 海大圖資處 圖書系統組
DSpace Software Copyright © 2002-2004  MIT &  Hewlett-Packard  /   Enhanced by   NTU Library IR team Copyright ©   - Feedback